LUPOY PC 1302-07 resin is designed for extrusion and injectionmolding products. It exhibits an excellent physical propertybalance of heat resistance, transparency and impact strength.
物性信息：
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| UL文件号 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
| 吸水率 | ASTM D570 | ||
| 23°C, 24hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C, 50%RH | 0.32 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 74 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2410 | MPa | ASTM D638 |
| 抗张强度 | ASTM D638 | ||
| 屈服 | 60.0 | MPa | ASTM D638 |
| 断裂 | 72.0 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 6.0 | % | ASTM D638 |
| 断裂 | 150 | % | ASTM D638 |
| 弯曲模量 | 2410 | MPa | ASTM D790 |
| 弯曲强度 | 96.0 | MPa | ASTM D790 |
| 耐磨耗性 - Change in Haze 1 | 45 | % | ASTM D1004 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 平均燃烧程度 | 3 | cm | ASTM D635 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 2(23°C,3.20 mm) | 900 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 无断裂 | ASTM D256 | |
| 装有测量仪表的落镖冲击 3(23°C,3.20 mm, Total Energy) | 90.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 退火, 4.00mm | 145 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 4.00mm | 129 | °C | ASTM D648 |
| 1.8 MPa, 退火, 4.00mm | 142 | °C | ASTM D648 |
| 维卡软化温度 | 151 | °C | ASTM D1525 4 |
| 球压温度 | > 125 | °C | IEC 60598-1 |
| 线形热膨胀系数 - 流动 (-40 到 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 (23°C) | 2.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 | 17 | kV/mm | ASTM D149 |
| 介电常数 (60 Hz) | 3.00 | ASTM D150 | |
| 耗散因数 (60 Hz) | 1.0E-3 | ASTM D150 | |
| 漏电起痕指数 (2.00 mm) | 250 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 0.500 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 2.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| 热灯丝点火温度 5(2.00mm) | 850 | °C | IEC 60695-2-13 |
| 极限氧指数 | 26 | % | ASTM D2863 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 折射率 | 1.586 | ASTM D542 | |
| 透射率 | 89.0 | % | ASTM D1003 |
| 雾度 | 0.70 到 1.5 | % | ASTM D1003 |